Thermo‐Mechanical Fatigue, Crack Evolution, and Fracture Reliability of Lightweight High‐Power‐Density Diesel Pistons: A Review
The higher power density and lightweight design of diesel pistons impose severe thermo‐mechanical demands. This review summarizes research on thermo‐mechanical fatigue, crack evolution, and fracture reliability in lightweight, high‐power‐density pistons. The review examines service loading, critical failure‐prone reg...