Study on the Influence of Recycled Aggregate Gradation, Fiber Reinforcement and Water-to-Cement Ratio on the Properties of Recycled Pervious Concrete
Abstract
To promote construction waste recycling and develop sustainable pavement materials, this study utilized recycled aggregates (crushing value 7.8%) obtained from bridge demolition as a 100% replacement for natural aggregates in recycled pervious concrete. The research focused on investigating the influence of different aggregate gradations (single-sized 4.75–9.5 mm and binary-graded combinations: 4.75–9.5 + 16–31.5 mm, 2–5 + 13–26.5 mm) and different water-to-cement ratios (0.26, 0.27, 0.30) on the concrete properties. Tests on compressive strength, splitting tensile strength, and connected porosity revealed the following results: The strength of recycled pervious concrete was comparable to that of natural aggregate concrete, and strength decreased with increasing aggregate size. The optimal water-to-cement ratio varied with gradation: 0.27 for the single-sized 4.75–9.5 mm aggregate and 0.30 for the binary-graded combinations. Splitting tensile strength was generally low, showed insignificant growth from 7 d to 28 d, was sensitive to interfacial defects, and exhibited high data variability. Connected porosity was inversely proportional to compressive strength and decreased with increasing water-to-cement ratio. This study provides experimental evidence for optimizing the preparation of high-performance recycled pervious concrete using recycled aggregates. In addition, the influence of fiber type, dosage, and length was preliminarily examined through an orthogonal design.